Methods of aligning a semiconductor wafer for singulation

ABSTRACT

Implementations of a method for aligning a semiconductor wafer for singulation may include: providing a semiconductor wafer having a first side and a second side. The first side of the wafer may include a plurality of die and the plurality of die may be separated by streets. The semiconductor wafer may include an edge ring around a perimeter of the wafer on the second side of the wafer. The wafer may also include a metal layer on the second side of the wafer. The metal layer may substantially cover the edge ring. The method may include grinding the edge ring to create an edge exclusion area and aligning the semiconductor wafer with a saw using a camera positioned in the edge exclusion area on the second side of the wafer. Aligning the wafer may include using three or more alignment features included in the edge exclusion area.

CROSS REFERENCE TO RELATED APPLICATIONS

This application claims the benefit of the filing date of U.S. Provisional Patent Application 62/796,687, entitled “METHODS OF ALIGNING A SEMICONDUCTOR WAFER FOR SINGULATION” to Seddon et al., which was filed on Jan. 25, 2019, the disclosure of which is hereby incorporated entirely herein by reference.

BACKGROUND 1. Technical Field

Aspects of this document relate generally to systems and methods used for aligning substrates for singulation. More specific implementations involve semiconductor substrates.

2. Background

Semiconductor substrates are used to form a wide variety of semiconductor devices. The semiconductor devices are generally distributed across a planar surface of the semiconductor substrate in a plurality of die. The plurality of die are separated from one another using a singulation process like sawing.

SUMMARY

Implementations of a method for aligning a semiconductor wafer for singulation may include: providing a semiconductor wafer having a first side and a second side. The first side of the wafer may include a plurality of die and the plurality of die may be separated by streets. The semiconductor wafer may include an edge ring around a perimeter of the wafer on the second side of the wafer. The wafer may also include a metal layer on the second side of the wafer. The metal layer may substantially cover the edge ring. The method may include grinding the edge ring to create an edge exclusion area and aligning the semiconductor wafer with a saw using a camera positioned in the edge exclusion area on the second side of the wafer. Aligning the wafer may include using two or more alignment features included in the edge exclusion area.

Implementations of methods for aligning a semiconductor wafer may include one, all, or any of the following:

The metal layer may include copper having a thickness of 15 microns.

The method may further include singulating the plurality of semiconductor die using one of sawing, lasering, or plasma etching.

The method may further include mounting the wafer to a picking tape.

Grinding the edge ring may further include washing debris from the wafer.

The metal layer may include one of gold, copper, nickel, or any combination thereof.

The camera may be an infrared camera and the semiconductor wafer may include silicon.

Implementations of a method for aligning a semiconductor wafer for singulation may include: providing a semiconductor wafer having a first side and a second side. The semiconductor wafer may include an edge ring around a perimeter of the wafer on the second side of the wafer. The method may include applying a metal coating to the second side of the wafer. The metal coating may extend substantially over the edge ring. The method may further include creating an edge exclusion area through removal of the edge ring. The method may also include aligning the wafer for singulation using an infrared camera. The infrared camera may use two or more alignment features in the edge exclusion area.

Implementations of methods for aligning a semiconductor wafer may include one, all, or any of the following:

The metal coating may be applied through one of sputtering, evaporation, or plating.

The method may further include mounting the wafer to a film frame.

The method may further include singulating a plurality of semiconductor die from the semiconductor wafer using one of sawing, lasering, and plasma etching.

The metal coating may have a thickness of at least 15 microns.

Removal of the edge ring may include grinding and washing the semiconductor wafer.

Singulating may include one of sawing, lasering, and plasma etching.

Implementations of a method for aligning a semiconductor wafer for singulation may include: mounting a first side of a semiconductor wafer to a backgrinding tape. The semiconductor wafer may include an edge ring around a perimeter of the wafer on a second side of the wafer. The method may also include applying a metal layer to the second side of the wafer. The metal layer may extend substantially over the edge ring. The metal layer may include grinding the edge ring and removing the metal layer in a perimeter area of the wafer. The method may include aligning the wafer for singulation using a camera and two or more alignment features in the perimeter area of the wafer.

Implementations of methods for aligning a semiconductor wafer may include one, all, or any of the following:

The metal layer may be applied through one of sputtering, evaporation, and plating.

The method may further include singulating a plurality of semiconductor die from the semiconductor wafer using a laser.

The metal layer may include copper having a thickness of 15 microns.

The removing the ring through grinding may further include washing debris from the wafer.

The camera may be an infrared camera and the semiconductor wafer may be silicon.

The foregoing and other aspects, features, and advantages will be apparent to those artisans of ordinary skill in the art from the DESCRIPTION and DRAWINGS, and from the CLAIMS.

BRIEF DESCRIPTION OF THE DRAWINGS

Implementations will hereinafter be described in conjunction with the appended drawings, where like designations denote like elements, and:

FIG. 1 is a side view of an implementation of a system for aligning a semiconductor wafer with a metal layer substantially covering an edge ring; and

FIG. 2 is a side view of an implementation of a system for aligning a semiconductor wafer with an implementation of an edge exclusion area formed via grinding; and

FIG. 3 is a front side view of an implementation of a semiconductor substrate/wafer.

DESCRIPTION

This disclosure, its aspects and implementations, are not limited to the specific components, assembly procedures or method elements disclosed herein. Many additional components, assembly procedures and/or method elements known in the art consistent with the intended methods of aligning a semiconductor wafer for singulation will become apparent for use with particular implementations from this disclosure. Accordingly, for example, although particular implementations are disclosed, such implementations and implementing components may comprise any shape, size, style, type, model, version, measurement, concentration, material, quantity, method element, step, and/or the like as is known in the art for such methods of aligning a semiconductor wafer for singulation, and implementing components and methods, consistent with the intended operation and methods.

For semiconductor die that are less than 50 microns in thickness, particular processing challenges exist. Die handling, die strength, and performing processing operations with the die all present specific challenges, as die and wafer breakage can significantly reduce yield and/or affect device reliability. Die strength is negatively affected by traditional singulation options like sawing which induce die chipping and cracking along the die streets. These chips and cracks formed during the sawing process can eventually propagate during operation and reliability testing causing the die to fail.

Referring to FIG. 1, a cross sectional side view of a substrate 2 coupled to a plurality of layers is illustrated. The term “substrate” refers to a semiconductor substrate as a semiconductor substrate is a common type of substrate, however, “substrate” is not an exclusive term that is used to refer to all semiconductor substrate types. Similarly, the term “substrate,” may refer to a wafer as a wafer is a common type of substrate, however, “substrate” is not an exclusive term that is used to refer to all wafers. The various semiconductor substrate types disclosed in this document that may be utilized in various implementations may be, by non-limiting example, round, rounded, square, rectangular, or any other closed shape. In various implementations, the substrate 2 may include a substrate material such as, by non-limiting example, single crystal silicon, silicon dioxide, glass, gallium arsenide, sapphire, ruby, silicon on insulator, silicon carbide, polycrystalline or amorphous forms of any of the foregoing, and any other substrate material useful for constructing semiconductor devices. In particular implementations, the substrate may be a silicon-on-insulator substrate.

Referring to FIGS. 1 and 3, in various implementations disclosed in this document, the semiconductor substrate 2 includes a plurality of semiconductor die 4 that have been processed using a semiconductor fabrication process to form one or more semiconductor devices therein or thereon (not shown). The die 4 may include multiple layers of metal such as, by non-limiting example, copper and aluminum. Each of the plurality of die may be separated by streets. The plurality of layers may be patterned, and in various implementations, may be patterned (or otherwise removed) to not be over a die street 24 in the substrate 2. The plurality of layers may include, by non-limiting example, one or more metal layers and, one or more passivation layers, any other layer, and any combination thereof. In various implementations, the plurality of die may include power semiconductor devices, such as, by non-limiting example, a metal oxide field effect transistor (MOSFET), an insulated gate bipolar transistor (IGBT), or any other power semiconductor device. In other implementations, the plurality of die may include non-power semiconductor devices.

Following the completion of the fabrication process (or during some portion of it, in some implementations), the semiconductor substrate 2 is thinned on a side 6 of the semiconductor substrate 2 that is opposite the side on which the one or more semiconductor devices 4 have been formed to a desired substrate thickness. The thinning process takes place using backgrinding, lapping, etching, any combination thereof, or any other technique for removing the material of the semiconductor substrate 2 substantially uniformly across the largest planar surface of the substrate.

In various implementations, the thinning process may create an edge ring 8 around the wafer (like that present in the backgrinding process marketed under the tradename TAIKO by Disco Hi-Tec America, Inc. of Santa Clara, Calif.). The edge ring acts to structurally support the wafer following thinning so that no wafer carrier may need to be utilized during subsequent processing steps. In various implementations, the thinning process may be carried out after the semiconductor substrate 2 has been mounted to a backgrinding tape 10. A wide variety of backgrinding tapes may be employed in various implementations, including those that are compatible with subsequent etching operations.

Following the thinning process, the various die 4 formed in the semiconductor substrate 2 need to be singulated from one another so they can be subsequently packaged into semiconductor packages. In various implementations, following the thinning process, a back metal layer 12 is applied to the semiconductor die through, by non-limiting example, sputtering, evaporation, or another metal deposition process or combination of processes. In various implementations, the deposition process is conducted while the wafer is either supported by an edge ring or supported by the backgrinding tape. In other implementations, however, the substrate may be demounted from the backgrinding tape and mounted to another support tape for subsequent processing steps. Singulation is performed by cutting/slicing the semiconductor substrate in the die streets between each of the plurality of die using any of the various method disclosed in this document.

The total thickness of the semiconductor substrate 2 is the additive product of the thickness of the substrate material, the thickness of any die 4 thereon, the thickness of the back metal 12, and the thickness of any passivation material thereon. In various implementations, thickness of the back metal may vary from between about 1 micron (μm) to about 15 μm. In particular implementations, the thickness of the back metal may be between about 1 μm to about 3 μm. In various implementations, the total thickness of the semiconductor substrate 2 may be less than about 50 μm. In particular implementations, the total thickness of the semiconductor substrate may be between about 25 μm to about 35 μm. In various implementations, the total thickness may be about 25 μm.

In various implementations, the substrate 2 may be thinned to a thickness less than 50 μm. In other implementations, the substrate 2 may be thinned to a thickness less than 30 μm. In still other implementations, the substrate 2 may be thinned to a thickness less than 100 μm, more than 100 μm, and in other various implementations, the substrate 2 may not be thinned. In particular implementations, the substrate 2 may be thinned to a thickness of about 25 μm, and in other particular implementations, the substrate may be thinned to a thickness of about 75 μm.

To singulate the plurality of die from the substrate, the substrate must be aligned with a set of predefined physical locations where a saw or other tool used for singulating the die will be cutting into the material of the substrate. In various implementations, a plurality of alignment features may be manufactured into the substrate to guide the singulation process. The alignment features may be formed in die streets positioned between the die and formed on the first side of the substrate. In other implementations, the alignment features may be formed on edges of the die. The alignment features may be located in any layer of the substrate. In various implementations, the alignment features may be located using an infrared camera. The infrared camera may be able to penetrate through layers of silicon or other materials to locate the alignment features. In other implementations, the alignment features may be located on an outer surface of the substrate. In some implementations, the alignment features may be visible with a visible light camera.

In various implementations, following the thinning process a back metal layer 12 is applied to the semiconductor die through, by non-limiting example, sputtering, evaporation, or another metal deposition process. In particular implementations, the backside metal layer 12 may be copper or a copper alloy. In other implementations, the backside metal layer may include any other type of metal, alloy thereof, or combination thereof. In various implementations, the backside metal layer may be about 10 μm thick. In other implementations, the backside metal layer may be more or less thick than 10 μm. The backside metal layer 12 may be evaporated onto the substrate 2, however, in other implementations (including implementations having thicker substrates), the backside metal layer 12 may be plated onto the substrate 2 or formed on the substrate using another technique.

Referring again to FIGS. 1 and 3, a semiconductor wafer 2 mounted on a backgrinding tape 10 is illustrated. The tape 10 may be supported by a film frame. A method of aligning a semiconductor wafer for singulation may include providing a semiconductor wafer 2 as illustrated. The semiconductor wafer 2 includes a plurality of die 4 formed on a first side of the wafer. The semiconductor wafer 2 has been thinned leaving an edge ring 8 around a perimeter 36 of the wafer 2. In various implementations, the wafer may be thinned as previously described through backgrinding. The method may include applying a metal coating 12 to a second side of the wafer. The metal coating may include, by non-limiting example, copper, nickel, gold, any combination thereof, alloys thereof, or other metals used in the metallization process. In one particular implementation of the method, the metal layer may include copper having a thickness of about 15 microns. In other implementations, the metal layer may have a thickness that is less than 15 microns. The method may include applying the metal coating through one of sputtering, plating, evaporation, or other methods used in applying a back metal to a semiconductor wafer. The metal coating 12 may extend substantially over the edge ring 8. When the metal coating 12 substantially covers the edge ring, a camera 14 focused on a second side of the wafer 2 is prevented from viewing past/through the metal coating. By non-limiting example, the metal layer may be covered by a patterned blanket of photoresist.

Referring to FIGS. 2 and 3, the substrate 2 is illustrated prepared for aligning the wafer by creating an edge exclusion area 16 located around/adjacent the perimeter 36 of the substrate 2 by removing the edge ring. The edge ring may be removed through grinding the metal layer and the material of the edge ring. Grinding the ring may also include washing debris from the wafer. Various implementations of the method may be used with substrates having thick back metal as well as thin back metal. In various implementations, a plurality of alignment features 30, 32, 34 may be included in the dimensions of edge exclusion area 16. In other implementations, at least two alignment features may be formed in the edge exclusion area. In other implementations, as illustrated in FIG. 3, three or more alignment features may be formed in the edge exclusion area. The method may further include aligning the wafer/substrate 2 for singulation using a camera 20 using at least two alignment features. In various implementations, the camera 20 may be an infrared camera and the wafer may be formed of silicon. The camera may be able to detect the alignment features in/through the silicon or other layered materials to align the wafer with a singulating tool. In various implementations, a vacuum check may not be needed in the alignment process.

In various implementations, referring to FIG. 2, the wafer may be singulated using a saw 22. In other implementations, the wafer may be singulated through lasering. Jet ablation may be used to singulate the wafer into a plurality of die in some implementations. In methods including grooving or thinning of the metal layer, plasma may be used to singulate the wafer into a plurality of die. In some implementations, a singulation step may be performed from a first side of the substrate or the second side of the substrate. For implementations where sawing or lasering is used for singulation, remote plasma healing may be performed on the singulated dies to remove sidewall damage. In various implementations, remote plasma healing may also be used to remove small amount of re-deposition.

Variations of this method may allow for active modifications/adjustments to the alignment of the wafer or the singulation process itself during the singulation process based on visual inspection. Non-limiting examples of possible modifications may include changes in laser power, changes in pulse of the laser, or changes in speed. The camera 20 may also be able to monitor the need to clear back metal/remaining back metal thickness. In various implementations, the camera may be used to measure any thickness variations of any ablated metal and the original thickness of the metal. Such monitoring may allow the adjustment of singulating parameters during the singulation process. In various implementations, the use of the alignment features in the edge exclusion area during the alignment process may not require to use of a vacuum check.

In places where the description above refers to particular implementations of method for wafer/substrate alignment and implementing components, sub-components, methods and sub-methods, it should be readily apparent that a number of modifications may be made without departing from the spirit thereof and that these implementations, implementing components, sub-components, methods and sub-methods may be applied to other methods for wafer alignment. 

What is claimed is:
 1. A method for aligning a semiconductor wafer for singulation, the method comprising: providing a semiconductor wafer having a first side and a second side, the first side of the wafer comprising a plurality of die, wherein the plurality of die are separated by streets, the semiconductor wafer comprising an edge ring around a perimeter of the semiconductor wafer on the second side of the semiconductor wafer, the semiconductor wafer further comprising a metal layer on the second side of the semiconductor wafer wherein the metal layer substantially covers the edge ring; grinding the edge ring to create an edge exclusion area; and aligning the semiconductor wafer with a saw using a camera positioned in the edge exclusion area on the second side of the semiconductor wafer using two of more alignment features comprised in the edge exclusion area.
 2. The method of claim 1, wherein the metal layer comprises copper having a thickness of 15 microns.
 3. The method of claim 1, further comprising singulating the plurality of die using one of sawing, lasering, or plasma etching.
 4. The method of claim 1, further comprising mounting the semiconductor wafer to a picking tape.
 5. The method of claim 1, wherein grinding further comprises washing debris from the semiconductor wafer.
 6. The method of claim 1, wherein the metal layer comprises one of gold, copper, nickel, or any combination thereof.
 7. The method of claim 1, wherein the camera is an infrared camera and the semiconductor wafer comprises silicon.
 8. A method for aligning a semiconductor wafer for singulation, the method comprising: providing a semiconductor wafer comprising a first side and a second side, the semiconductor wafer comprising an edge ring around a perimeter of the semiconductor wafer on the second side of the semiconductor wafer; applying a metal coating to the second side of the semiconductor wafer, wherein the metal coating extends substantially over the edge ring; creating an edge exclusion area through removal of the edge ring; and aligning the semiconductor wafer for singulation using an infrared camera, wherein the infrared camera uses two or more alignment features in the edge exclusion area.
 9. The method of claim 8, wherein the metal coating is applied through one of sputtering, evaporation, or plating.
 10. The method of claim 8, further comprising mounting the semiconductor wafer to a film frame.
 11. The method of claim 8, further comprising singulating a plurality of semiconductor die from the semiconductor wafer using one of sawing, lasering, or plasma etching.
 12. The method of claim 8, wherein the metal coating has a thickness of at least 15 microns.
 13. The method of claim 8, wherein removal of the edge ring comprises grinding and washing the semiconductor wafer.
 14. The method of claim 8, further comprising thinning the semiconductor wafer to form the edge ring.
 15. A method for aligning a semiconductor wafer for singulation, the method comprising: mounting a first of a semiconductor wafer to a backgrinding tape, the semiconductor wafer comprising an edge ring around a perimeter of the semiconductor wafer on a second side of the semiconductor wafer; applying a metal layer to the second side of the semiconductor wafer, wherein the metal layer extends substantially over the edge ring; grinding the edge ring and removing the metal layer in a perimeter area of the semiconductor wafer; aligning the semiconductor wafer for singulation using a camera and two or more alignment features in the perimeter area of the semiconductor wafer.
 16. The method of claim 15, wherein the metal layer is applied through one of sputtering, evaporation, and plating.
 17. The method of claim 15, further comprising singulating a plurality of die from the semiconductor wafer using a laser.
 18. The method of claim 15, wherein the metal layer comprises copper having a thickness of 15 microns.
 19. The method of claim 15, wherein the removing the edge ring through grinding further comprises washing debris from the semiconductor wafer.
 20. The method of claim 15, wherein the camera is an infrared camera and the semiconductor wafer is silicon. 